Jen-D Radiance Molar Bulkfill Composite 4 gm A2

Jen-Radiance Molar is a light-cured, radiopaque fluoride-containing composite restorative material. It is intended for sealing of I and II class cavities. The material Jen-Radiance Molar possesses high degree of transparency and very low shrinkage at polymerization (1.63%) which makes it possible to draw it by layers up to 5 mm thick with the minimum polymerization stress. The material is very soft, can be perfectly modelled and it also adapts in a cavity, filling all roughnesses. It doesn’t stick to a dental instrument.

• The high filler content of material (82%) provided by a new formula of a bimodal filler with an average size of particles: the main X-ray contrast phase – up to 8 microns; a nanophase – 10-30 nanometers.
• It can be perfectly combined with all types of opaque and enamel composite materials based on methacrylate intended for esthetic modeling of enamel surfaces.
• Low polymerization shrinkage (less than 1.63%) is especially important when a dentist seals big cavities in one visit.
• Good manual qualities – the material is very soft and plastic and doesn’t stick to the tool.
• The Coefficient of Thermal Expansion (CTE) is very close to tooth tissue – 24 x 10 – 6 cm / cm oC that provides the absence of thermal stresses in the restored tooth, which can appear during the meal (“hot-cold”).
• High physical characteristics of the material, in particular:
  
  • Flexural Strength – 120 MPa.
  • Compression Strength – 270 MPa.
• It is manufactured in a universal transparent shade – U for ensuring the maximum depth of polymerization.
• Not cured material has the increased resistance to natural and artificial lighting that allows to carry out long modeling without risk of premature polymerization of the material.
• The material is radiopaque and contains fluorine